DUPONT IMRON 3.4 HG-C POLYURETHANE -
PART "A" ONLY Imron 3.4 HG-C high gloss clear aliphatic polyurethane enamel is a high-solids, two-package, VOC conforming product (3.4 lbs./gal.), producing properties of both polyester and acrylic polyurethanes. The resulting highly durable finish delivers industry leading polyurethane performance. Brush, roll or spray. (FORMERLY IMRON 610P). Product is sold by the gallon. 4 gallons in a case.
Activator VG610 is sold separately.
MIXING AND REDUCTION
Thoroughly mix 3 parts Imron 3.4 HG-C (610P) Enamel, then add 1 part Imron VG-610 Activator while stirring. No induction period is necessary.
Normally 0-3% (1-4 oz.) reduction is adequate for spray application depending upon conditions and equipment. Maximum reduction should not exceed 3%. Use DuPont 68083 Thinner. If faster recoat and handling is required, add up to 2 oz./gal VG-805 Accelerator.
SURFACE PREPARATION
Newly primed surfaces should be clean and dry. If contaminated, detergent/water wash, then blow dry. Previously painted surfaces should have all loose paint removed and the edges feathered. Prime bare spots with appropriate primer.
APPLICATION CONDITIONS
This product is best applied by spray. Do not apply if the application surface temperature is below 45°F (7°C) or above 110°F (43°C), or if the atmospheric temperature is within 5°F of the dew point. For best results, application temperature should be between 65°F and 85°F. Relative Humidity should be below 90%. For application temperatures below 45°F, the use of VG-805 Accelerator is required. Mix only amounts that can be applied within a 1.5 – 2 hour period. For airless spray application, tip size must not exceed .011”.
Theoretical Coverage: 834 ft² (20.5 m²/L) @ 1 mil -- 556 ft² (13.6 m²/L) @ suggested DFT of 1.5 mils
Suggested Film Build: 3 – 4 mils (75 – 100 μm) wet (WFT) -- 1.5 – 2 mils (37 – 50 μm) dry (DFT)